316L Dur Di-staen - Gwrthsefyll Cyrydiad
Feb 26, 2026
Gadewch neges
Cyfansoddiad Cemegol Dur Di-staen 316
Tabl 1 .Cyfansoddiad cemegol nodweddiadol ar gyfer 316 o aloion dur di-staen
% | 316 | 316L | 316H | 316Ti |
C | 0.0-0.07 | 0.0-0.03 | 0.04-0.08 | 0.0- 0.08 |
Mn | 0.0-2.0 | 0-2.0 | 0.0-2.00 | 0.0-2.00 |
Si | 0.0-1.0 | 0.0-1.00 | 0.0-1.00 | 0.0- 1.00 |
P | 0.0-0.05 | 0.0-0.05 | 0-0.04 | 0.0-0.05 |
S | 0.0-0.02 | 0.0-0.02 | 0.0-0.02 | 0.0-0.03 |
Cr | 16.50-18.50 | 16.50-18.50 | 16.50-18.50 | 16.50- 18.50 |
Mo | 2.00-2.50 | 2.00-2.50 | 2.00-2.50 | 2.00- 2.50 |
Ni | 10.00-13.00 | 10.00-13.00 | 10.00-13.00 | 10.50- 14.00 |
Ti | - | - | - | 0.40- 0.70 |
Fe | cydbwysedd | cydbwysedd | cydbwysedd | cydbwysedd |
Priodweddau Dur Di-staen 316
Priodweddau Mecanyddol Dur Di-staen 316
Tabl 2 .Priodweddau mecanyddol nodweddiadol ar gyfer 316 o aloion dur di-staen
Gradd | 316 Bar ac Adran (hyd at 160 mm o drwch) | Dalen 316 (hyd at 8 mm o drwch) | Plât 316 (8 - 75 mm o drwch) | Bar ac Adran 316L (hyd at 160 mm) | Dalen 316L (hyd at 8 mm o drwch) | Plât 316 L (8 - 75 mm o drwch) | Bar 316H (hyd at 160 mm) | 316Ti Bar(hyd at 160 mm) |
Cryfder Tynnol (MPa) | 500 - 700 | 530 - 680 | 520 - 670 | 500 - 700 | 530 - 680 | 520 - 670 | 490 - 690 | 500 - 700 |
Prawf Straen (MPa) | 200 Munud | 240 Munud | 220 Munud | 200 Munud | 240 Munud | 220 Munud | 205 Min | 200 Munud |
Elongation A50 mm | 40 Munud % | 40 Munud % | 45 Munud % | 40 Munud % | 40 Munud % | 45 Munud % | 35 % | 40 Munud % |
Caledwch Brinell | 215 Uchafswm HB | - | - | 215 Uchafswm HB | - | - | - | 215 Uchafswm HB |