Premiwm AISI 304H Dur Di-staen o Gnee
Mar 23, 2026
Gadewch neges
🧪 Cyfansoddiad Cemegol
| Elfen | Cyfansoddiad (%) |
|---|---|
| carbon (C) | 0.04 - 0.10 |
| Manganîs (Mn) | Llai na neu'n hafal i 2.00 |
| silicon (Si) | Llai na neu'n hafal i 0.75 |
| Ffosfforws (P) | Llai na neu'n hafal i 0.045 |
| sylffwr (S) | Llai na neu'n hafal i 0.030 |
| Cromiwm (Cr) | 18.0 - 20.0 |
| Nicel (Ni) | 8.0 - 10.5 |
| Nitrogen (N) | Llai na neu'n hafal i 0.10 |
| Haearn (Fe) | Cydbwysedd |
⚙️ Priodweddau Mecanyddol
| Eiddo | Gwerth |
|---|---|
| Cryfder tynnol (min) | 515 MPa |
| Cryfder Cynnyrch 0.2% Gwrthbwyso (munud) | 205 MPa |
| Hydiad mewn 50mm (munud) | 40% |
| Lleihau Arwynebedd (isafswm) | 50% |
| Caledwch (Brinell) | Llai na neu'n hafal i 201 HB |
| Caledwch (Rockwell B) | Llai na neu'n hafal i 92 HRB |
| Effaith Egni (Charpy V-rhicyn o 20 gradd ) | Yn fwy na neu'n hafal i 120 J |
| Terfyn Blinder (10^7 cylchred) | 240 MPa |
| Modwlws Elastigedd | 200 GPa |
🔬 Priodweddau Corfforol
| Eiddo | Gwerth |
|---|---|
| Dwysedd | 8.00 g / cm³ |
| Ymdoddbwynt | 1400-1450 gradd |
| Dargludedd Thermol ( ar 100 gradd ) | 16.2 W/m·K |
| Cyfernod Ehangu Thermol (20-100 gradd) | 17.2×10-6/K |
| Cynhwysedd Gwres Penodol | 500 J/kg·K |
| Gwrthiant Trydanol ( 20 gradd ) | 0.72 µΩ·m |
| Athreiddedd Magnetig | 1.02 (An-magnetig) |
| Trylededd Thermol | 4.2×10-6 m²/s |
| Tymheredd Curie | Dd/B (Awstenitig) |
📏 Manylebau Cynnyrch
| Manyleb | Opsiynau sydd ar Gael |
|---|---|
| Ffurflenni Cynnyrch | Platiau, Taflenni, Coiliau, Bariau, Gwialenni, Tiwbiau, Pibellau, Gofaniadau |
| Trwch Plât | 6mm - 200mm |
| Trwch Taflen | 0.4mm - 6mm |
| Diamedr Bar | 6mm - 300mm |
| Diamedr Allanol Tiwb | 6mm - 610mm |
| Safonau | ASTM A240, A479, A312, EN 10088-2, JIS G4305, GB/T 3280 |
| Gorffen Arwyneb | 2B, BA, Rhif 4, HL (Hairline), Drych, piclo |
| Goddefgarwch | ±0.1mm (trwch), ±3mm (lled), ±6mm (hyd) |
| Cyflwr Ymyl | Ymyl y Felin, Ymyl Hollt, Ymyl Trimiedig |
| Triniaeth Gwres | Ateb wedi'i Anelio (1040-1120 gradd) |