🧪 Cyfansoddiad Cemegol
| Elfen | Cyfansoddiad (%) |
|---|---|
| carbon (C) | Llai na neu'n hafal i 0.08 |
| Manganîs (Mn) | Llai na neu'n hafal i 2.00 |
| silicon (Si) | Llai na neu'n hafal i 0.75 |
| Ffosfforws (P) | Llai na neu'n hafal i 0.045 |
| sylffwr (S) | Llai na neu'n hafal i 0.030 |
| Cromiwm (Cr) | 17.0 - 20.0 |
| Nicel (Ni) | 9.0 - 13.0 |
| niobium (Nb) | 10 × C min, 1.00 max |
| Haearn (Fe) | Cydbwysedd |
⚙️ Priodweddau Mecanyddol
| Eiddo | Gwerth |
|---|---|
| Cryfder Tynnol (Tymheredd Ystafell) | Yn fwy na neu'n hafal i 515 MPa |
| Cryfder Cynnyrch (Gwrthbwyso 0.2%) | Yn fwy na neu'n hafal i 205 MPa |
| Elongation mewn 50mm | Mwy na neu'n hafal i 40% |
| Caledwch (Brinell) | Llai na neu'n hafal i 217 HB |
| Caledwch (Rockwell B) | Llai na neu'n hafal i 95 HRB |
| Effaith Egni (Charpy V-rhicyn, 20 gradd) | Yn fwy na neu'n hafal i 120 J |
| Terfyn Blinder (107beiciau) | 240 MPa |
| Modwlws Young | 200 GPa |
🔬 Priodweddau Corfforol
| Eiddo | Gwerth |
|---|---|
| Dwysedd | 7.95 g / cm³ |
| Ymdoddbwynt | 1400-1450 gradd |
| Dargludedd Thermol (20 gradd) | 14.2 W/m·K |
| Cyfernod Ehangu Thermol (20-100 gradd) | 17.3×10-6/K |
| Cynhwysedd Gwres Penodol | 500 J/kg·K |
| Gwrthiant Trydanol ( 20 gradd ) | 0.73 µΩ·m |
| Athreiddedd Magnetig | 1.02 (Paramagnetig) |
| Cymhareb Poisson | 0.27-0.30 |
📏 Manylebau Cynnyrch
| Ffurflen Cynnyrch | Meintiau Ar Gael | Safonau |
|---|---|---|
| Platiau Rholio Poeth | Trwch: 6-100mm, Lled: hyd at 2500mm | ASTM A240, ASME SA-240 |
| Taflenni Rholio Oer | Trwch: 0.4-6mm, Lled: hyd at 1500mm | ASTM A240, EN 10088-2 |
| Bariau Crwn | Diamedr: 6-300mm, Hyd: hyd at 6000mm | ASTM A276, ASTM A479 |
| Tiwbiau di-dor | OD: 6-610mm, WT: 1-60mm | ASTM A213, ASTM A312 |
| Pibellau Wedi'u Weldio | OD: 10-1220mm, WT: 1-40mm | ASTM A312, ASTM A358 |
| Gorffeniadau Arwyneb | 2B, BA, Rhif 4, HL, Drych | ASTM A480 |
| Goddefgarwch Dimensiynol | ±0.1mm i ±0.5mm | Yn unol â Safonau ASTM |