Dur Di-staen AISI 410 yn Tsieina ar gyfer custome
Mar 23, 2026
Gadewch neges
🧪 Cyfansoddiad Cemegol
| Elfen | Cyfansoddiad (%) |
|---|---|
| carbon (C) | ≤ 0.15 |
| Manganîs (Mn) | ≤ 1.00 |
| silicon (Si) | ≤ 1.00 |
| Ffosfforws (P) | ≤ 0.040 |
| sylffwr (S) | ≤ 0.030 |
| Cromiwm (Cr) | 11.5 - 13.5 |
| Nicel (Ni) | ≤ 0.75 |
| Haearn (Fe) | Cydbwysedd |
⚙️ Priodweddau Mecanyddol
| Eiddo | Cyflwr Annealed | Wedi caledu a thymheru |
|---|---|---|
| Cryfder Tynnol | 485-620 MPa | 725-850 MPa |
| Cryfder Cynnyrch (gwrthbwyso 0.2%) | 275-415 MPa | 550-690 MPa |
| Hydiad (50mm) | ≥ 20% | ≥ 15% |
| Lleihau Ardal | ≥ 50% | ≥ 45% |
| Caledwch (Brinell) | 155-217 HB | 235-285 HB |
| Caledwch (Rockwell C) | - | 22-32 HRC |
| Impact Energy (Charpy V-rhif) | 54-81 J | 27-54 J |
| Terfyn Blinder (10&sup7; cylch) | 240 MPa | 360 MPa |
🔬 Priodweddau Corfforol
| Eiddo | Gwerth |
|---|---|
| Dwysedd | 7.75 g / cm³ |
| Ymdoddbwynt | 1480-1530°C |
| Gwres Penodol (20 ° C) | 460 J/kg·K |
| Dargludedd Thermol (100°C) | 24.9 W/m·K |
| Ehangu Thermol (20-100°C) | 9.9×10-6/K |
| Ehangu Thermol (20-500 ° C) | 11.2×10-6/K |
| Gwrthiant Trydanol (20°C) | 0.57 µΩ·m |
| Athreiddedd Magnetig | Ffromagnetig |
| Modwlws Elastigedd | 200 GPa |
| Cymhareb Poisson | 0.27-0.30 |
📏 Manylebau Cynnyrch
| Ffurflen Cynnyrch | Ystod Maint | Safonau |
|---|---|---|
| Bariau Crwn | 6-300mm diamedr | ASTM A276, A479 |
| Bariau Sgwâr | 10-150mm | ASTM A276 |
| Bariau Fflat | 3-100mm o drwch, hyd at 300mm o led | ASTM A276 |
| Taflenni | 0.5-6mm o drwch, hyd at 2000mm o led | ASTM A240 |
| Platiau | 6-100mm o drwch, hyd at 3000mm o led | ASTM A240 |
| Tiwbiau | 6-219mm OD, wal 0.5-20mm | ASTM A268 |
| Gorffen Arwyneb | Wedi'i rolio'n boeth, wedi'i dynnu'n oer, wedi'i sgleinio | 2B, BA, Rhif 4, Rhif 8 |
| Goddefgarwch | ±0.1mm i ±1.0mm | EN 10029, ASTM A480 |